Chemical composition % of grade CuSn12Ni2-C ( CC484K )
A suffix -C is added to the designation to identify material in the form of castings |
Fe | Si | Mn | Ni | P | S | Al | Cu | Pb | Zn | Sb | Sn |
max 0.2 | max 0.01 | max 0.2 | 1.5 - 2.5 | 0.05 - 0.4 | max 0.05 | max 0.01 | 84.5 - 87.5 | max 0.3 | max 0.4 | max 0.1 | 11 - 13 |
New opportunities for buyers!
Post free buying requirement for CuSn12Ni2-C
Mechanical properties of grade CuSn12Ni2-C ( CC484K )
Rm - Tensile strength (MPa) (GS) | 280 |
Rm - Tensile strength (MPa) (GZ) or (GC) | 300 |
Rp0.2 0.2% proof strength (MPa) (GS) | 160 |
Rp0.2 0.2% proof strength (MPa) (GZ) or (GC) | 180 |
A - Min. elongation at fracture (%) (GS) | 12 |
A - Min. elongation at fracture (%) (GZ) | 8 |
A - Min. elongation at fracture (%) (GC) | 10 |
Brinell hardness (HBW): (GS) | 85 |
根据ASTM B505 / B505M-18化学成分
注意:铜+命名元素的总和,最小值99.5%。单值,除非特别指出,代表最大值。
抗拉强度(N / mm2) 590
证明/屈服强度(N / mm2) 230
伸长率(%) 12
硬度布氏硬度 150
悬臂梁式冲击J 20 15°c
密度g / cm3 7.45
熔化温度范围 1027 - 1037°c
导热系数W /可 58.7
电阻率μΩ。 m15°c 0.13
热膨胀系数 0 - 250°c 16.2
相对磁导率 1.2
摩擦系数