LLDPE 中石化广州 DNDA-7144瓶盖 涂覆  

 

陶氏线性低密度聚乙烯 DNDA-7144 NT 7

Linear Low Density Polyethylene Resin

The Dow Chemical Company

产品说明：

• Injection molding

• Large industrial containers and trash cans

• Excellent low temperature impact strength, rigidity, stress crack resistance and processability

• Very narrow molecular weight distribution

• Complies with

• U.S. FDA 21 CFR 177.1520 (c)3.1a

• CANDIAN HPFB NO OBJECTION ( WITH LIMITATIONS)

• EU, No 10/2011

• U.S. FDA -DMF

• Consult the regulations for complete details.

DOW DNDA-7144 NT 7 Linear Low Density Polyethylene (LLDPE) Resin is produced using UNIPOL™ PE Process Technology and is intended for use in injection molding applications such as large industrial containers and trash cans. This resin has been designed to have excellent impact strength, rigidity, environmental stress crack resistance and processability.

附加功能

 

陶氏线性低密度聚乙烯 DNDA-7144 NT 7 物性表

基本信息
机构评级	DMF 未评级 FDA 21 CFR 177.1520(c) 3.1a HPFB (加拿大) No Objection 2 欧洲 No 10/2011
形式	粒子
加工方法	注射成型

物理性能	额定值	单位制	测试方法
比重	0.924	g/cm3	ASTM D792
熔流率（熔体流动速率） (190°C/2.16 kg)	20	g/10 min	ASTM D1238
抗环境应力开裂 (50°C, 100% Igepal, F50)	20.0	hr	ASTM D1693

硬度	额定值	单位制	测试方法
肖氏硬度 (邵氏 D)	50		ASTM D2240

机械性能	额定值	单位制	测试方法
抗张强度			ASTM D638
屈服	11.7	MPa	ASTM D638
断裂	7.58	MPa	ASTM D638
伸长率			ASTM D638
屈服	3.0	%	ASTM D638
断裂	60	%	ASTM D638
弯曲模量 - 2% 正割	386	MPa	ASTM D790B

冲击性能	额定值	单位制	测试方法
拉伸冲击强度 1	168	kJ/m2	ASTM D1822

热性能	额定值	单位制	测试方法
载荷下热变形温度 (0.45 MPa, 未退火)	42.8	°C	ASTM D648
脆化温度	< -76.1	°C	ASTM D746
维卡软化温度	93.9	°C	ASTM D1525
溶融温度（DSC）	123	°C	内部方法
结晶峰温度 (DSC)	108	°C	内部方法

补充信息
根据 ASTM D 4976 进行基板模制和测试。

备注
1 .	类型 S