SABIC Innovative Plastics NORYL GFN1720
Polymer,Thermoplastic,Polyphenylene Ether/PPO,Polystyrene (PS)
SABIC Innovative Plastics (GE Plastics)
产品说明:
Noryl* GFN1720 is a 20% glass fiber reinforced, injection moldable grade. This modified polyphenylene ether resin is designed to deliver a balance of heat, strength and electrical properties. Noryl GFN1720 is available in multiple colors and may be an excellent material candidate for ignition coils, bobbins and other application requiring electrically insulating properties.
SABIC Innovative Plastics NORYL GFN1720
物理性能额定值 (公制)额定值 (英制)测试方法
比重 | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
密度 | 1.24 g/cc | 0.0448 lb/in3 | ISO 1183 |
水分吸收 | 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 |
饱和吸水率 | 0.15 % | 0.15 % | ISO 62 |
线性成型收缩率,Flow | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | on Tensile Bar; SABIC Method |
0.0020 - 0.0040 cm/cm @Thickness 3.20 mm | 0.0020 - 0.0040 in/in @Thickness 0.126 in | SABIC Method | |
熔体流动速率 | 4.5 g/10 min @Load 5.00 kg, Temperature 300 °C | 4.5 g/10 min @Load 11.0 lb, Temperature 572 °F | ASTM D1238 |
化合物熔体指数 | 11 g/10 min @Load 10.0 kg, Temperature 300 °C | 11 g/10 min @Load 22.0 lb, Temperature 572 °F | MVR [cm^3/10 min]; ISO 1133 |
机械性能额定值 (公制)额定值 (英制)测试方法
硬度,H358/30 | 100 MPa | 14500 psi | ISO 2039-1 |
抗张强度(断裂) | 90.0 MPa | 13100 psi | Type I, 5 mm/min; ASTM D638 |
90.0 MPa | 13100 psi | 5 mm/min; ISO 527 | |
抗张强度(屈服) | 90.0 MPa | 13100 psi | Type I, 5 mm/min; ASTM D638 |
90.0 MPa | 13100 psi | 5 mm/min; ISO 527 | |
伸长率 (断裂) | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 | |
屈服伸长率 | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
2.5 % | 2.5 % | Type I, 5 mm/min; ASTM D638 | |
拉伸模量 | 5.50 GPa | 798 ksi | 5 mm/min; ASTM D638 |
6.00 GPa | 870 ksi | 1 mm/min; ISO 527 | |
弯曲强度 | 135 MPa | 19600 psi | 2 mm/min; ISO 178 |
145 MPa | 21000 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
弯曲模量 | 4.50 GPa | 653 ksi | 2 mm/min; ISO 178 |
4.80 GPa | 696 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
悬壁梁缺口冲击强度 | 0.600 J/cm | 1.12 ft-lb/in | ASTM D256 |
0.500 J/cm @Temperature -30.0 °C | 0.937 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
悬壁梁无缺口冲击强度 | 25.0 kJ/m2 | 11.9 ft-lb/in2 | 80*10*4; ISO 180/1U |
25.0 kJ/m2 @Temperature -30.0 °C | 11.9 ft-lb/in2 @Temperature -22.0 °F | 80*10*4; ISO 180/1U | |
简支梁无缺口冲击强度 | 2.50 J/cm2 | 11.9 ft-lb/in2 | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
2.50 J/cm2 @Temperature -30.0 °C | 11.9 ft-lb/in2 @Temperature -22.0 °F | Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
落锤总能量 | 14.0 J @Temperature 23.0 °C | 10.3 ft-lb @Temperature 73.4 °F | ASTM D3763 |
泰伯磨损,毫克/1000次 | 45 | 45 | CS-17, 1 kg; SABIC Method |
电气性能额定值 (公制)额定值 (英制)测试方法
体积电阻率 | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
表面电阻 | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
介电常数 | 2.6 @Frequency 1.00e+6 Hz | 2.6 @Frequency 1.00e+6 Hz | IEC 60250 |
2.7 @Frequency 50.0 - 60.0 Hz | 2.7 @Frequency 50.0 - 60.0 Hz | IEC 60250 | |
介电强度 | 16.0 kV/mm @Thickness 3.20 mm | 406 kV/in @Thickness 0.126 in | in oil; IEC 60243-1 |
26.0 kV/mm @Thickness 1.60 mm | 660 kV/in @Thickness 0.0630 in | in oil; IEC 60243-1 | |
30.0 kV/mm @Thickness 0.800 mm | 762 kV/in @Thickness 0.0315 in | in oil; IEC 60243-1 | |
耗散因数 | 0.0020 @Frequency 1.00e+6 Hz | 0.0020 @Frequency 1.00e+6 Hz | IEC 60250 |
0.0060 @Frequency 50.0 - 60.0 Hz | 0.0060 @Frequency 50.0 - 60.0 Hz | IEC 60250 | |
相比耐漏电起痕指数(CTI) | 200 V | 200 V | IEC 60112 |
热性能额定值 (公制)额定值 (英制)测试方法
线形热膨胀系数 - 流动 | 30.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 16.7 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 |
40.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 22.2 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
线性热膨胀系数,横向流动 | 50.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 27.8 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
70.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 38.9 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | |
导热系数 | 0.260 W/m-K | 1.80 BTU-in/hr-ft2-°F | ISO 8302 |
Hot Ball Pressure Test | <= 165 °C | <= 329 °F | IEC 60695-10-2 |
载荷下热变形温度(0.46 MPa) | 170 °C | 338 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
载荷下热变形温度(1.8 MPa) | 160 °C | 320 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
171 °C @Thickness 3.20 mm | 340 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
维卡软化温度 | 170 °C | 338 °F | Rate B/50; ISO 306 |
180 °C | 356 °F | Rate B/120; ISO 306 | |
180 °C | 356 °F | Rate A/50; ISO 306 | |
181 °C | 358 °F | Rate B/50; ASTM D1525 | |
UL RTI | 65.0 °C | 149 °F | UL 746B |
UL RTI,机械冲击 | 65.0 °C | 149 °F | UL 746B |
UL RTI,机械无冲击 | 65.0 °C | 149 °F | UL 746B |
可燃性(UL94) | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | UL 94 |
HB @Thickness 3.00 mm | HB @Thickness 0.118 in | UL 94 | |
极限氧指数 | 23 % | 23 % | ISO 4589 |
灼热丝试验 | 960 °C @Thickness 3.20 mm | 1760 °F @Thickness 0.126 in | IEC 60695-2-12 |
材料描述 测试方法
Ball Pressure Test, 125?°C +/- 2?°C | PASSES | IEC 60695-10-2 |